DSpace Repository

Redistribution of Nickel Ions Embedded within Indium Phosphide Via Low Energy Dual Ion Implantations

Show simple item record

dc.contributor.author Jones, Daniel C.
dc.contributor.author Young, Joshua M.
dc.contributor.author Lakshantha, Wickramaarachchige J
dc.contributor.author Singh, Satyabrata
dc.contributor.author . Byers, Todd A
dc.contributor.author . Weathers, Duncan L
dc.contributor.author . McDaniel, Floyd D
dc.contributor.author Rout, Bibhudutta
dc.date.accessioned 2022-04-13T08:00:33Z
dc.date.available 2022-04-13T08:00:33Z
dc.date.issued 2018-08-06
dc.identifier.issn 2321-8649
dc.identifier.issn 2321-9289
dc.identifier.uri http://dspace.chitkarauniversity.edu.in/xmlui/handle/123456789/368
dc.description.abstract Transition-metal doped Indium Phosphide (InP) has been studied over several decades for utilization in optoelectronics applications. Recently, interesting magnetic properties have been reported for metal clusters formed at different depths surrounded by a high quality InP lattice. In this work, we have reported accumulation of Ni atoms at various depths in InP via implantation of Ni- followed by H– and subsequently thermal annealing. Prior to the ion implantations, the ion implant depth profile was simulated using an ion-solid interaction code SDTrimSP, incorporating dynamic changes in the target matrix during ion implantation. Initially, 50 keV Ni- ions are implanted with a fluence of 2 × 1015 atoms cm-2, with a simulated peak deposition profile approximately 42 nm from the surface. 50 keV H- ions are then implanted with a fluence of 1.5 × 1016 atoms cm-2. The simulation result indicates that the H- creates damages with a peak defect center ~400 nm below the sample surface. The sample has been annealed at 50°C in an Ar rich environment for approximately 1hr. During the annealing, H vacates the lattice, and the formed nano-cavities act as trapping sites and a gettering effect for Ni diffusion into the substrate. The distribution of Ni atoms in InP samples are estimated by utilizing Rutherford Backscattering Spectrometry and X-ray Photoelectron Spectroscopy based depth profiling while sputtering the sample with Ar-ion beams. In the sample annealed after H implantation, the Ni was found to migrate to deeper depths of 125 nm than the initial end of range of 70 nm. en_US
dc.language.iso en en_US
dc.relation.ispartofseries ;CHAENG/2013/51628
dc.subject Ni nanoclusters en_US
dc.subject Dual Ion Implantations en_US
dc.subject Rutherford Backscattering en_US
dc.subject Rutherford Backscattering en_US
dc.title Redistribution of Nickel Ions Embedded within Indium Phosphide Via Low Energy Dual Ion Implantations en_US
dc.type Article en_US